Aida Aluminum Titanium Boron

Color code

Ti

B

Fe

Si

V

Other each

Other total

Balance

AlTi5B1

4.5-5.5

0.8-1.2

≤0.25

≤0.20

≤0.05

≤0.03

≤0.10

Aluminum

AlTi5B1
(class A)

Ti:

4.8~5.2

In any 1cm² vertical section, the average size of TiB₂ particles is < 2µm, and there can be no more than 3 TiB₂ loose clusters with a size of < 25µm; the average size of TiAl₃ particles is < 30µm, and the maximum size of a single particle is < 150µm

In any 1cm² vertical section, the total length of Al₂O₃ and salt attachments is <1000µm. There are no forms of boride and undissolved solid impurities.

Double zero foil and hot rolled strip for CTP printing, plates for beverage cans, AA and A flaw detection products and important engineering aluminum and aluminum alloy materials, which require high internal organization.

B:

0.9~1.1

Fe:

≦0.20

Si:

≦0.15

V:

≦0.05

AlTi5B1
(class B)

Ti:

4.5~5.5

In any 1cm² vertical section, the average size of TiB₂ particles is ≦ 2µm, and there can be no more than 6 TiB₂ loose clusters with a size of < 50µm; the average size of TiAl₃ particles is < 50µm, and the maximum size of a single particle is < 200µm

In any 1cm² vertical section, the total length of Al₂O₃ and salt attachments is <3000µm. There are no forms of boride and undissolved solid impurities.

Single zero foil, PS plate base (including color printing, general printing), deep drawing sheet, 1xxx, 3xxx, 5xxx and 8xxx alloy processed products.

B:

0.8~1.2

Fe:

≦0.25

Si:

≦0.20

V:

≦0.05

AlTi5B1
(class C)

Ti:

4.5~5.5

In any 1cm² vertical section, the average size of TiB₂ particles is ≦ 5µm, and the size of TiB₂ loose clusters is not restricted; the average size of TiAl₃ particles is < 50µm, and the maximum size of a single particle is < 200µm

In any 1cm² vertical section, the total length of Al₂O₃ and salt attachments is not restricted. There are no forms of boride and undissolved solid impurities.

2xxx, 4xxx, 7xxx alloy processed products and general cast rod products.

B:

0.4~1.2

Fe:

≦0.30

Si:

≦0.20

V:

≦0.05